The difference between the T5 and T6 in aluminium plate
What is the difference between the T5 and T6 states in the aluminum brazing plate
state?
Before explaining the difference between the T5 and T6 states, the user must first understand the following two noun explanations:
Aging: The process of eliminating internal stress in metals.
Quenching: The metal is heated to a certain temperature and suddenly cooled to meet the required hardness. 2, 6, 7 series aluminum plates can be strengthened by quenching treatment.
The T5 state means that the aluminum sheet plate is extruded from the extruder and then air-cooled to rapidly reduce the temperature to achieve the desired hardness requirement (8--12 hardness of Webster). The T6 state means that the aluminum plate is extruded from the extruder and then cooled by water to cool the aluminum plate instantaneously, so that the aluminum plate reaches a higher hardness requirement (above 13.5 hardness).
The use of air-cooling and cooling is relatively long, usually 2-3 days, we call it natural aging; and the water cooling time is short, we call it artificial aging. The main difference between the aluminum plate T5 T6 states is that the intensity of the T6 state is higher than that of the T5 state, and the performance of other aspects is similar. In terms of price, because of the difference in production process, the price of T6 aluminum plate per ton is higher than that of T5.
What is the elimination of internal stress
In the production process, the aluminum plate is uneven in density due to heat and extrusion, and the energy is not completely released, and is accumulated inside the aluminum plate. This energy is called internal stress. Some users production processes (such as heating, bending, deep drawing, stretching, etc.) will release the internal stress of the aluminum plate, causing the aluminum plate to bend, wave, and surface inequality, so it is necessary to release the internal stress of the aluminum plate.
The process of eliminating internal stress is very simple. After the aluminum plate goes down the assembly line, the aluminum product manufacturer will add a process, and the machine will stretch the aluminum plate to release the energy inside the aluminum plate.
The state of the aluminum plate for eliminating internal stress is represented by the number Tx51, such as: aluminum sheet plate 6061 T651, 6082 T651, and the like.
The 6000 seres aluminum plate is an aluminum-magnesium-silicon alloy, and its
representative grades are 6061, 6063 and 6082 aluminium. Different from the
other seven aluminum plates, the state of the 6-series aluminum plate is
dominated by the T state, and the most is the T5 and T6 states. There is only
one word difference. What is the difference between these two states?
Before explaining the difference between the T5 and T6 states, the user must first understand the following two noun explanations:
Aging: The process of eliminating internal stress in metals.
Quenching: The metal is heated to a certain temperature and suddenly cooled to meet the required hardness. 2, 6, 7 series aluminum plates can be strengthened by quenching treatment.
The T5 state means that the aluminum sheet plate is extruded from the extruder and then air-cooled to rapidly reduce the temperature to achieve the desired hardness requirement (8--12 hardness of Webster). The T6 state means that the aluminum plate is extruded from the extruder and then cooled by water to cool the aluminum plate instantaneously, so that the aluminum plate reaches a higher hardness requirement (above 13.5 hardness).
The use of air-cooling and cooling is relatively long, usually 2-3 days, we call it natural aging; and the water cooling time is short, we call it artificial aging. The main difference between the aluminum plate T5 T6 states is that the intensity of the T6 state is higher than that of the T5 state, and the performance of other aspects is similar. In terms of price, because of the difference in production process, the price of T6 aluminum plate per ton is higher than that of T5.
What is the elimination of internal stress
In the production process, the aluminum plate is uneven in density due to heat and extrusion, and the energy is not completely released, and is accumulated inside the aluminum plate. This energy is called internal stress. Some users production processes (such as heating, bending, deep drawing, stretching, etc.) will release the internal stress of the aluminum plate, causing the aluminum plate to bend, wave, and surface inequality, so it is necessary to release the internal stress of the aluminum plate.
The process of eliminating internal stress is very simple. After the aluminum plate goes down the assembly line, the aluminum product manufacturer will add a process, and the machine will stretch the aluminum plate to release the energy inside the aluminum plate.
The state of the aluminum plate for eliminating internal stress is represented by the number Tx51, such as: aluminum sheet plate 6061 T651, 6082 T651, and the like.